PEEK Rod
PEEK is a high-performance thermoplastic that is tough, durable, firm, and creep resistant.
It offers excellent thermal, chemical, and hydrolysis resistance as well as excellent
resistance to abrasion and dynamic fatigue. Its ability to run at high continuous
temperatures up to (250º C) without permanent property degradation along with stable
electrical properties makes PEEK an excellent alternative to fluoropolymers in aggressive
environments. PEEK has also been shown to exhibit very low smoke and toxic gas emission when
exposed to flame.
PEEK rod is the most common PEEK shape that is suitable for machining, CNC, grinding and
nearly all other processing way.
JUNHUA ChinaPEEK offers the most diversed PEEK rod dimensions in the world, JUNHUA ChinaPEEK
offers PEEK rod from dia 3mm up to dia 260mm. PEEK rods are avaiable in PEEK Natural, PEEK
Black, 30% Glass fiber filled PEEK, 30% Carbon fiber filled PEEK, and bearing grade PEEK(10%
PTFE,10% Carbon fiber,10% Graphite,70% PEEK).
Main Advantages of PEEK Rod
- ● Good wearing performance with or without load
- ● High service temperature(long term 260C
- ● Good mechanical strength
- ● Good chemical resistance & Hydrosis resistance
- ● FDA approved
PEEK5600G (unfilled PEEK or natural PEEK)
PEEK5600G is one of unfilled or natural PEEK.Outstanding chemical resistance and a high operating temperature (up to 250℃/480F) round out PEEK profile.PEEK5600G has excellent dimensional stability combined with high creep stability, ensuring the suitability of PEEK for the most sophisticated machined parts.
PEEK5600GF30 ( 30% glass fiber filled PEEK)
Compared with unfilled PEEK(PEEK5600G),this 30% glass fiber reinforced PEEK material(PEEK5600GF30) exhibits increased mechanical strength and high rigidity.Plus, improved creep strength and dimensional stability are delivered by the 30% glass fiber filled PEEK.
PEEK5600CF30 (30% carbon fiber filled PEEK)
PEEK5600CF30 is a 30% carbon filled PEEK material that is manufactured by JUNHUA PEEK. Its carbon fiber reinforcement supports the material a high level of rigidity. Carbon fiber reinforced PEEK demonstrates very high mechanical strength values.
PEEK5600LF30( HPV PEEK or bearing grade PEEK)
PEEK5600LF30 black is developed especially for bearing and sliding applications. HPV PEEK is based on a PEEK polymer that has been modified with 10% each of PTFE, graphite and carbon fibres. It combines the properties of a high-grade matrix material with special, wear-improving additives.
PEEK Solutions
PEEK Solutions
PEEK is widely used in a variety of industries. We offer our solution by provideing material (whether as raw material, semi-finished products or as precisely processed finished parts) and technical guidance based on our knowledge and experience. Our experts will always be happy to assist you with your industry and application.
Aerospace
Food
Mechanical
Medical
Oil and Gas
Semiconductor
Contact us for more information and services.
Contact us Now, Get a Quote, Product Manual, Performance Parameters, Custom Solutions, Technical Consultation, and Samples for PEEK Materials!
PEEK Rod Typical Data
| Item | Standard | Data | Units |
| Color | - | Natural | |
| Density | ISO 1138 | 1.3±0.01 | g/cm3 |
| Water Absorption (25℃.24Hrs) | ISO 62 | 0.05 % | |
| Melting temperature | ISO 11357 | 343 | ℃ |
| Distortion Temperature | ISO 75-1/-2 | 163 | ℃ |
| Continuous service Temperature | UL 74685 | 260 | ℃ |
| Thermal expansion coefficient | ASTM D696 | 4.7*10-6 | /K |
| Tensile Strength (23℃) | ISO 527 | 100 | MPa |
| Tensile modulus (23℃) | ISO 527 | 3.8 | GPa |
| Tensile Elongation (23℃) | ISO 527 | 27 % | |
| Bending Strength (23℃) | ISO 178 | 163 | MPa |
| Bending Modulus (23℃) | ISO 178 | 3.5 | GPa |
| Impact Strength(23℃) | ISO 604 | 123 | MPa |
| Lzod Impact Strength (No notched) | ISO 180/U | No Break | kJ/m2 |
| Poisson Ratio | ISO 527-2 | 0.4 | |
| Rockwell Hardness | GB3398.2 | 118 | |
| Flammability | UL 94 (1.5 mm) | V-0 | |
| Dielectric strength | IEC 60243-1 | 18 | KV/mm |
| Dielectric constant | IEC 60250 | 3.2 | |
| Thermal Conductivity | ISO 22007 | 0.28 | W/(m·K) |
| Surface Resistance | IEC 90093 | 1015 | Ω |
| Item | Standard | Data | Units |
| Color | - | Black | |
| Density | ISO 1138 | 1.4±0.03 | g/cm3 |
| Water Absorption (25℃.24Hrs) | ISO 62 | 0.05 % | |
| Melting temperature | ISO 11357 | 343 | ℃ |
| Distortion Temperature | ISO 75-1/-2 | 315 | ℃ |
| Continuous service Temperature | UL 74685 | 260 | ℃ |
| Thermal expansion coefficient | ASTM D696 | 1.5*10-6 | /K |
| Tensile Strength (23℃) | ISO 527 | 125 | MPa |
| Tensile modulus (23℃) | ISO 527 | 9.3 | GPa |
| Tensile Elongation (23℃) | ISO 527 | 2.5 % | |
| Bending Strength (23℃) | ISO 178 | 271 | MPa |
| Bending Modulus (23℃) | ISO 178 | 9.1 | GPa |
| Impact Strength(23℃) | ISO 604 | 196 | MPa |
| Lzod Impact Strength (No notched) | ISO 180/U | 38 | kJ/m2 |
| Poisson Ratio | ISO 527-2 | 0.35 | |
| Rockwell Hardness | GB3398.2 | 123 | |
| Flammability | UL 94 (1.5 mm) | V-0 | |
| Dielectric strength | IEC 60243-1 | - | KV/mm |
| Dielectric constant | IEC 60250 | - | |
| Thermal Conductivity | ISO 22007 | 0.95 | W/(m·K) |
| Surface Resistance | IEC 90093 | 105 | Ω |
| Item | Standard | Data | Units |
| Color | - | Natural | |
| Density | ISO 1138 | 1.5±0.01 | g/cm3 |
| Water Absorption (25℃.24Hrs) | ISO 62 | 0.05 % | |
| Melting temperature | ISO 11357 | 343 | ℃ |
| Distortion Temperature | ISO 75-1/-2 | 315 | ℃ |
| Continuous service Temperature | UL 74685 | 260 | ℃ |
| Thermal expansion coefficient | ASTM D696 | 2.2*10-6 | /K |
| Tensile Strength (23℃) | ISO 527 | 110 | MPa |
| Tensile modulus (23℃) | ISO 527 | 7.9 | GPa |
| Tensile Elongation (23℃) | ISO 527 | 3.5 % | |
| Bending Strength (23℃) | ISO 178 | 214 | MPa |
| Bending Modulus (23℃) | ISO 178 | 7.5 | GPa |
| Impact Strength(23℃) | ISO 604 | 142 | MPa |
| Lzod Impact Strength (No notched) | ISO 180/U | 41 | kJ/m2 |
| Poisson Ratio | ISO 527-2 | 0.35 | |
| Rockwell Hardness | GB3398.2 | 122 | |
| Flammability | UL 94 (1.5 mm) | V-0 | |
| Dielectric strength | IEC 60243-1 | 17 | KV/mm |
| Dielectric constant | IEC 60250 | 3.4 | |
| Thermal Conductivity | ISO 22007 | 0.31 | W/(m·K) |
| Surface Resistance | IEC 90093 | 1015 | Ω |
| Item | Standard | Data | Units |
| Color | - | Black | |
| Density | ISO1138 | 1.44±0.05 | g/cm3 |
| WaterAbsorption(25℃.24Hrs) | ISO62 | 0.05% | |
| Meltingtemperature | ISO11357 | 343 | ℃ |
| DistortionTemperature | ISO75-1/-2 | 315 | ℃ |
| ContinuousserviceTemperature | UL74685 | 260 | ℃ |
| Thermalexpansioncoefficient | ASTMD696 | 2.4*10-6 | /K |
| TensileStrength(23℃) | ISO527 | 70 | MPa |
| Tensilemodulus(23℃) | ISO527 | 4.0 | GPa |
| TensileElongation(23℃) | ISO527 | 2.5% | |
| BendingStrength(23℃) | ISO178 | 100 | MPa |
| BendingModulus(23℃) | ISO178 | 4.0 | GPa |
| ImpactStrength(23℃) | ISO604 | 135 | MPa |
| LzodImpactStrength(Nonotched) | ISO180/U | 26 | |
| PoissonRatio | ISO527-2 | 0.35 | |
| RockwellHardness | GB3398.2 | 120 | |
| Flammability | UL94(1.5mm) | V-0 | |
| Dielectricstrength | IEC60243-1 | - | KV/mm |
| Dielectricconstant | IEC60250 | - | |
| ThermalConductivity | ISO22007 | 0.86 | W/(m·K) |
| SurfaceResistance | IEC90093 | 105 | Ω |
PEEK Rod Stock Program
| Diameter(mm) | Tolerance(mm) | Standard Length(mm) | Weight per 1000mm(kg) |
| 3 | -0,+0.8 | 1000/3000 | 0.012 |
| 4 | -0,+0.8 | 1000/3000 | 0.021 |
| 5 | -0,+0.8 | 1000/3000 | 0.035 |
| 6 | -0,+0.8 | 1000/3000 | 0.043 |
| 8 | -0,+0.8 | 1000/3000 | 0.078 |
| 10 | -0,+0.8 | 1000/3000 | 0.12 |
| 12 | -0,+0.8 | 1000/3000 | 0.165 |
| 13 | -0,+0.8 | 1000/3000 | 0.18 |
| 15 | -0,+0.8 | 1000/3000 | 0.255 |
| 16 | -0,+1 | 1000/3000 | 0.29 |
| 18 | -0,+1 | 1000/3000 | 0.36 |
| 20 | -0,+1 | 1000/3000 | 0.46 |
| 22 | -0,+1 | 1000/3000 | 0.53 |
| 25 | -0,+1.2 | 1000/3000 | 0.68 |
| 28 | -0,+1.2 | 1000/3000 | 0.84 |
| 30 | -0,+1.2 | 1000/3000 | 1 |
| 32 | -0,+1.2 | 1000/3000 | 1.13 |
| 35 | -0,+1.2 | 1000/3000 | 1.35 |
| 38 | -0,+1.2 | 1000/3000 | 1.56 |
| 40 | -0,+1.5 | 1000/3000 | 1.79 |
| 45 | -0,+1.5 | 1000/3000 | 2.22 |
| 50 | -0,+1.5 | 1000/3000 | 2.73 |
| 53 | -0,+1.5 | 1000/3000 | 2.99 |
| 55 | -0,+1.5 | 1000/3000 | 3.28 |
| 60 | -0,+2 | 1000/3000 | 3.96 |
| 65 | -0,+2 | 1000/3000 | 4.54 |
| 70 | -0,+2 | 1000/3000 | 5.43 |
| 75 | -0,+2 | 1000/3000 | 6.08 |
| 80 | -0,+2.5 | 1000/3000 | 7.02 |
| 85 | -0,+2.5 | 1000/3000 | 7.68 |
| 90 | -0,+2.5 | 1000/3000 | 8.75 |
| 93 | -0,+2.5 | 1000/3000 | 9.27 |
| 95 | -0,+2.5 | 1000/3000 | 9.55 |
| 100 | -0,+2.5 | 1000/3000 | 10.97 |
| 105 | -0,+2.5 | 1000/3000 | 11.65 |
| 110 | -0,+2.5 | 1000/3000 | 13.4 |
| 115 | -0,+2.5 | 1000/3000 | 13.99 |
| 120 | -0,+2.5 | 1000/3000 | 15.7 |
| 125 | -0,+2.5 | 1000/3000 | 16.45 |
| 130 | -0,+2.5 | 1000/3000 | 18.39 |
| 140 | -0,+2.5 | 1000/3000 | 20.89 |
| 150 | -0,+2.5 | 1000/3000 | 24.45 |
| 160 | -0,+2.5 | 1000/3000 | 27.2 |
| 165 | -0,+2.5 | 1000/3000 | 28.9 |
| 170 | -0,+2.5 | 1000/3000 | 31.1 |
| 180 | -0,+3 | 1000/3000 | 34.4 |
| 190 | -0,+3 | 1000/3000 | 38.2 |
| 200 | -0,+3 | 1000/3000 | 42.28 |
| 220 | -0,+3 | 1000 | 51.53 |
| 250 | -0,+4 | 1000 | 66.8 |
| 260 | -0,+5 | 1000 | 72.77 |
Certificate
Certificate & Compliance
Certificate
JUNHUA Focus on PEEK Material
JUNHUA PEEK Business Unit operates in a way that accelerates the deep plowing of PEEK downstream applications. JUNHUA PEEK currently has 6,000+ customers, and its revenue growth rate in 2021 exceeds 50%, of which the revenue growth rate in the medical field exceeds 80%. It is worth mentioning that JUNHUA medical division has become an independent subsidiary.18 + Years
Leading peek manufacturer since 2007.
70+ Countries
It is exported to the USA, Germany, South Korea, and more than 70 other countries and regions.
50,000+ Clients
After continuous accumulation, the total number of customers in various industries over 50,000.
500,000+ Products
Dig Industry demand, statistics have done 500000 kinds of PEEK parts and other products.
- Fast Delivery
- Efficiency & Cost-saving
- 24/7 Customer Service
- Life-long technical support
Contact
Contact Us
Fill the Form to Get a Quote, Product Manual, Performance Parameters, Custom Solutions, Technical Consultation, and Samples for PEEK Materials!